Intergard® 400 is a two pack epoxy abrasion resistant coating, containing micaceous iron oxide, which can be overcoated after extended periods.
As a general purpose primer for all non-permanently immersed areas.For use at Newbuilding.
|Colour||EPA001-MIO Dark Grey, EPA007-MIO Light Grey|
|Part B (Curing Agent)||EPA740|
|Volume Solids||65% ±2% (ISO 3233:1998)|
|Typical Film Thickness||125 microns dry (192 microns wet)|
|Theoretical Coverage||5.2 m²/litre at 125 microns dft, allow appropriate loss factors |
|Method of application||Airless Spray, Roller, Brush|
|Flammpunkt||Part A 23°C |
Part B 23°C
¹ EU Solvent Emissions Directive (Council Directive 1999/13/EC)
|Surface Temperature||0 °C||5 °C||25°C||35 °C|
|Touch Dry [ISO 9117/3:2010]||12 hrs||3 hrs||2 hrs||1 hr|
|Hard Dry [ISO 9117-1:2009]||1.5 d||1.5 d||12 hrs||8 hrs|
|Pot Life||13 hrs||12 hrs||6 hrs||2 hrs|
For additional information about Overcoating Data see "Overcoating Data" in the Technical Data Sheet.
When used as part of an approved scheme, this material has the following certification:
• Food Contact - Carriage of Grain (NOHA)
• Fire Resistance - Surface Spread of Flame (Exova Warringtonfire)
• Fire Resistance - Smoke & Toxicity (Exova Warringtonfire)
• Fire Resistance - Marine Equipment Directive compliant
Consult your International Paint representative for details.
Systems and compatibility
Consult your International Paint representative for the system best suited for the surfaces to be protected.
Use in accordance with the standard Worldwide Marine Specifications.All surfaces to be coated should be clean, dry and free from contamination.High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning.
Where necessary, remove weld spatter and smooth weld seams and sharp edges.Weld seams and areas of shop primer damage or breakdown should be blast cleaned to Sa2½ (ISO 8501-1:2007) or power tooled to Pt3 (JSRA SPSS:1984).
Intact shop primers must be clean, dry and free from soluble salts and any other surface contaminants.If the shop primer shows extensive or widely scattered breakdown, overall sweep blasting may be necessary.Consult your International Paint representative for specific recommendations.
When overcoating with Intergard 410, Intergard 415 and Intergard 740 the anticipated level of intercoat adhesion can only be achieved in "extended" overcoating situations when:
a) the aged coating has the "extended" surface characteristics required for long term overcoatability. For example, an over applied epoxy MIO may not have its usual "textured" surface and will no longer be overcoatable after ageing unless it is abraded.
b) the coating to be overcoated is intact, tightly adherent, clean, dry and free of all contaminants.
c) coatings with a glossy surface are treated by light surface abrasion, sweep blasting or other suitable processes which do not cut through or detract from the performance of the underlying coating.
Consult your International Paint representative for specific recommendations.
|Mixing||Material is supplied in 2 containers as a unit. Always mix a complete unit in the proportions supplied. |
(1) Agitate Base (Part A) with a power agitator.
(2) Combine entire contents of Curing Agent (Part B) with Base (Part A) and mix thoroughly with power agitator.
|Mix Ratio||5.67 volume(s) Part A to 1 volume(s) Part B|
|Airless Spray||Recommended |
Tip Range 0.46-0.58 mm (18-23 thou)
Total output fluid pressure at spray tip not less than 176 kg/cm² (2500 p.s.i.)
|Conventional Spray||Application by conventional spray is not recommended.|
|Brush||Application by brush is recommended for small areas only. Multiple coats may be required to achieve specified film thickness.|
|Roller||Application by roller is recommended for small areas only. Multiple coats may be required to achieve specified film thickness.|
|Thinner||International GTA220. Thinning is not normally required. Consult the local representative for advice during application in extreme conditions. Do not thin more than allowed by local environmental legislation.|
|Work Stoppages and Cleanup||Do not allow material to remain in hoses, gun or spray equipment. Thoroughly flush all equipment with International GTA822. Once units of paint have been mixed they should not be resealed and it is advised that after prolonged stoppages work recommences with freshly mixed units. |
Clean all equipment immediately after use with International GTA822. It is good working practice to periodically flush out spray equipment during the course of the working day. Frequency of cleaning will depend upon amount sprayed, temperature, relative humidity and elapsed time, including any delays. Do not exceed pot life limitations.All surplus materials and empty containers should be disposed of in accordance with appropriate regional regulations/legislation.
|Welding||In the event welding or flame cutting is performed on metal coated with this product, dust and fumes will be emitted which will require the use of appropriate personal protective equipment and adequate local exhaust ventilation. In North America do so in accordance with instruction in ANSI/ASC Z49.1 "Safety in Welding and Cutting."|
All work involving the application and use of this product should be performed in compliance with all relevant national Health, Safety & Environmental standards and regulations.
Prior to use, obtain, consult and follow the Material Safety Data Sheet for this product concerning health and safety information. Read and follow all precautionary notices on the Material Safety Data Sheet and container labels. If you do not fully understand these warnings and instructions or if you can not strictly comply with them, do not use this product. Proper ventilation and protective measures must be provided during application and drying to keep solvent vapour concentrations within safe limits and to protect against toxic or oxygen deficient hazards. Take precautions to avoid skin and eye contact (ie. gloves, goggles, face masks, barrier creams etc.) Actual safety measures are dependant on application methods and work environment.
Emergency contact numbers can be found in the Technical Data Sheet (TDS)
This product will not cure adequately below 0°C. For maximum performance ambient curing temperature should be above 5°C.
Optimum performance is achieved when Intergard 400 is applied over blasted steel.
Overcoating information is given for guidance only and is subject to regional variation depending upon local climate and environmental conditions. Consult your local International Paint representative for specific recommendations.Apply in good weather. Temperature of the surface to be coated must be at least 3°C above the dew point. For optimum application properties bring the material to 21-27°C, unless specifically instructed otherwise, prior to mixing and application. Unmixed material (in closed containers) should be maintained in protected storage in accordance with information given in the STORAGE Section of this data sheet. Technical and application data herein is for the purpose of establishing a general guideline of the coating application procedures. Test performance results were obtained in a controlled laboratory environment and International Paint makes no claim that the exhibited published test results, or any other tests, accurately represent results found in all field environments. As application, environmental and design factors can vary significantly, due care should be exercised in the selection, verification of performance and use of the coating.In the overcoating data section 'ext' = extended overcoating period. Please refer to our Marine Painting Guide - Definitions and Abbreviations available on our website
|Volume (Liters)||Pack (Liters)|
|Intergard® 400 Part A||17||20|
|Intergard® 400 Part B||3||5|
Storage and Lifetime
Lifetime at 25 °C
minimum 12 Month(s)
Subject to re-inspection thereafter. Store in dry, shaded conditions away from sources of heat and ignition.
Diese Angaben stammen aus dem offiziellen Technischen Datenblatt von dem Lackhersteller. Wir übernehmen keine Gewährleistung für die Richtigkeit / fehlerhafte Angaben.
Wir bitten Sie, sich ausschließlich ans Technische Datenblatt des Herstellers zu halten, welches Sie weiter unten als PDF-Download finden.
All information were taken out of the Technical Data Sheet provided by the manufacturer. We don't garantuee the correctness of any information.
Please adhere solely to the Technical Data Sheet provided by the manufacturer which you can download as a PDF-File further below.